Product |
Notes |
Hardness |
Mix |
Pot |
Demold |
Mixed |
Cured |
Tensile |
Name |
And Typical |
|
Ratio |
Life |
Time |
Viscosity |
Color |
Strength |
|
Uses |
|
[by Volume] |
|
|
|
|
[psi] |
Molding
Urethanes (Castable) |
|
|
|
|
|
|
|
*EP1150 |
Cast Concrete & Plaster |
50 A |
1:1 |
6 min |
2.5 h |
700 cps |
waxy white |
320 |
VytaFlex 10 |
Sculpture/Architectural. |
10 A |
1:1 |
30 min |
16 h |
3100 cps |
off-white |
160 |
VytaFlex 20 |
Concrete Molds |
20 A |
1:1 |
30 min |
16 h |
1,000 cps |
Clear Amber |
200 |
VytaFlex 30 |
Concrete Molds. |
30 A |
1:1 |
30 min |
16 h |
1,800 cps |
Off White |
500 |
VytaFlex 40 |
Prototype/Model Molds |
40 A |
1:1 |
30 min |
16 h |
2,000 cps |
Off White |
522 |
VytaFlex 50 |
Prototype/Model Molds. |
50 A |
1:1 |
60 min |
16 h |
2,000 cps |
off-white |
588 |
VytaFlex 60 |
For more firm Molds |
60 A |
1:1 |
60 min |
16 h |
2,000 cps |
Off White |
880 |
ReoFlex 20 |
Good for Gypsums |
20 A |
1:1 |
30 min |
16 h |
1,800 cps |
Off White |
200 |
*PMC121-30, Wet |
Good for Plaster; |
30 A |
1:1 |
30 min |
16 h |
1,800 cps |
clear amber |
400 |
*PMC121-50, Wet |
Plaster & Gypsums |
50 A |
1:1 |
30 min |
16 h |
1,400 cps |
clear amber |
350 |
*ReoFlex 40, |
cement and plaster] |
40 A |
1:1 |
30 min |
16 h |
1,500 cps |
Off White |
490 |
*PMC724 |
Popular jewelery-making rubber |
40 A |
1:10 (Wt) |
20 min |
16 h |
4,000 cps |
ivory |
600 |
*ReoFlex 60 |
Firm/Minimal Undercuts |
60 A |
1:10 (Wt) |
50 min |
16 h |
1,800 cps |
Off White |
782 |
*PMC744 |
For Plaster |
40 A |
2:1 (Wt/Vol) |
15 min |
16 h |
3.400 cps |
clear amber |
300 |
*PMC746 |
For Plaster |
60 A |
2:1 (Wt/Vol) |
15 min |
16 h |
1,200 cps |
clear amber |
700 |
PMC760 |
For Plaster |
60 A |
2:1 (Wt) |
15 min |
16 h |
2,800 cps |
clear amber |
350 |
*PMC780 |
For Abrasives |
80 A |
2:1 (Wt/Vol) |
30 min |
16 h |
2,000 cps |
light amber |
900 |
*PMC790 |
For Concrete |
90 A |
2:1 (Wt/Vol) |
20 min |
16 h |
3,000 cps |
light amber |
2000 |
PMC860 |
For Plaster & Concrete |
60 A |
2:1 (Wt/Vol) |
20 min |
16 h |
2,000 cps |
pine |
900 |
PMC870 |
|
70 A |
2:1 (Wt) |
35 min |
16 h |
3,000 cps |
light amber |
750 |
Molding
urethanes can also be cast into molds to make flexible parts |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Brush-On
Compounds |
|
|
|
|
|
|
|
BO35 |
[Easily paints on vertical |
35 A |
1:1 |
20 min |
16 h |
light paste |
green |
|
*BO40 |
surfaces without running. |
40 A |
1:1 |
20 min |
16 h |
light paste |
off-white |
|
*BO50 |
Can be used for on-site architectural |
50 A |
1:1 |
20 min |
16 h |
light psate |
off-white |
|
BO60 |
restoration. No Bubbles.] |
60 A |
1:1 |
20 min |
16 h |
light paste |
off-white |
|
*Flexwax |
Low melt wax. Replicate Body Parts |
|
one-component |
1 min |
4 min |
light paste |
blue |
|
Alginate |
Natural material. For lifecasting |
|
Mix w/ water |
1.5 min |
4.5 min |
light paste |
cream |
|
*Latex |
Safe to use. Brush one layer / day |
|
one-component |
<10 min |
12 h |
light paste |
light tan |
|
EZ-Mix |
Similar to BO50 |
50 A |
1:1 |
|
|
|
|
|
EZ-Spray |
For Spray Machine |
50 A |
1:1 |
|
|
|
|
|
*Denotes Stock
Item |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|